super fast-cure series eva film
su406&su806
product introduction
f•rst® su406 & su806 eva is a super fast-cure type encapsulant product. the lamination time can be decreased to 10min~12min when modules are encapsulated using su406/su806 eva. while the pv module productivity can be greatly increased with su406 & su806 eva, excellent durability, as well as pid and snail trails resistance will be exhibited.
crosslinking property
performance parameter
| properties | test method | units | su406 | su806 | |
| general gram weight | fst method | g/m2 | 430±20 | 390±20 | |
| thickness | fst method | mm | 0.55±0.05 | 0.50±0.05 | |
| length | fst method | m/roll | 150 | 150 | |
| width | fst method | mm | customization0/ 7 | customization0/ 7 | |
| density | astmd792 | g/cm3 | 0.95-0.96 | 0.95-0.96 | |
| melting range | fst method | ℃ | 40-80 | 40-80 | |
| shrinkage rate(120℃,3min) | gb/t29848 | md% | <3.0 | <3.0 | |
| td% | <1.5 | <1.5 | |||
| uv-cutoff wavelength | fst method | nm | -- | 360 | |
| transmittance | 1100nm-380nm | gb/t29848 | % | >91 | >91 |
| 380nm-290nm | % | >80 | <30 | ||
| gel content | gb/t29848 | gel% | >75 | >75 | |
| volume resistivity | gb/t29848 | ω·cm | >1.0×1015 | >1.0×1015 | |
| strength of peeling from glass | gb/t29848 | n/cm | >60 | >60 | |
| strength of peeling from tpt | gb/t29848 | n/cm | >40 | >40 | |